Maysa Artissiani, Nuni Widiarti, Sri Wahyuni, Endah Widhihastuti, Neli Syahida Ni’ma
The ability of inorganic antibacterial agents like metal oxides and nanoscale inorganic materials to inhibit bacterial growth rates has yet to receive much research attention. In this study, CaCO3-ZnO/Y-zeolite nanocomposites were created utilizing coprecipitation and impregnation techniques with Ca(CH3COO)2, Zn(CH3COO)2•2H2O, Y-zeolite precursors. Physical and chemical characteristics of nanocomposites have been investigated using XRD, FTIR, and SEM-EDX characterizations. The agar-well diffusion method tested the substance for antibacterial activity against gram-positive and gram-negative bacteria. Nanocomposites have a crystal size range of 35.46-36.53 nm and a crystallinity of 35-37 %, according to the results of XRD analysis. The carbonate groups are visible in FTIR data at wave numbers 1433, 875, and 712 cm-1. The Zn-O absorption band was verified at wave numbers 600-400 cm-1. The Y-zeolite absorption bands at wave numbers 1012-997 cm-1 and 745-746 cm-1 were confirmed. The particle morphology is cube-shaped with irregular sizes. The EDX result showed that the composition consists of 35.92 % calcium, 1.68 % zinc, 44.81 % oxygen, and 13.79 % carbon as elements. With the addition of 2.5 % Y-zeolite, the antibacterial activity of nanocomposites showed the best results, with an inhibition zone diameter of 7.62 mm against Escherichia coli and 6.56 mm against Staphylococcus aureus bacteria. © 2024, Published By Jurnal Kimia Valensi.
Department of Chemistry, Faculty of Mathematics and Natural Science, Universitas Negeri Semarang, Semarang, 50229, Indonesia; Department of Pharmacy, Faculty of Medicine, Universitas Negeri Semarang, Semarang, 50237, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock