Masturi, Dante Alighiri, Widya Nurul Jannah, Riful Mazid Maulana, Ulul Amri, Susilawati, Sunarno
A leaves waste biocomposite was produced via a simple mixing and hot-pressing process. Using mango (Mangifera indica L.) leaves waste as a filler and polyvinyl acetate (PVAc) as a binder, the biocomposite was synthesized at pressure and temperature of 3 metric tons and 40°C, respectively, for 20 minutes. The weight fraction of leaves waste varied obtaining a composite having maximum compressive strength, i.e., 37.82 MPa for leaves waste fraction of 0.62 (w/w). This strength is comparable to several stones such as sandstone stone, limestone, clay brick, aspen wood, and pinewood usually used as building materials. Therefore, the biocomposite is acceptable for building materials application. © 2020, Malaysian Society of Applied Biology. All rights reserved.
Physics Department, Faculty of Mathematics and Natural Sciences, Universitas Negeri Semarang, Indonesia; Chemistry Department, Faculty of Mathematics and Natural Sciences, Universitas Negeri Semarang, Indonesia; Physics Department, Faculty of Science and Technology, Universitas Islam Negeri Walisongo, Semarang, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock