Sulhadi, F. Usriyah, E. Wibowo, B. Astuti, Sugianto, D. Aryanto, P. Marwoto
Ga-doped ZnO (ZnO:Ga) thin films have been deposited on Corning glass substrates by handmade dc magnetron sputtering. The pressure and deposition time respectively were set on 500 mTorr and 60 minutes. The deposition temperature was fixed at 300°C with 30 watts of plasma power. The deposited ZnO:Ga thin films were heated at 300°C, 350°C, and 400°C, respectively. The morphology and crystallinity of ZnO:Ga thin films have been observed with SEM and XRD. The observation with SEM shows that the film morphology is denser and the grain size is smaller when the temperature is increased. The crystallinity of the film increases as the annealing temperature is enhanced from 300°C to 350°C. However, the crystallinity of the ZnO:Ga films decreased when the annealing temperature is 400°C. © 2019 Published under licence by IOP Publishing Ltd.
Physics Department, Universitas Negeri Semarang, Semarang, 50229, Indonesia; Engineering Physics, School of Electrical Engineering, Telkom University, Bandung, Indonesia; Research Center for Physics, Lembaga Ilmu Pengetahuan Indonesia (LIPI), Serpong, 15314, Indonesia
Research at a Glance
Register to unlock
Topics & SDG Alignment
Register to unlock
Collaboration
Register to unlock
Author Profile (Selected)
Register to unlock
References Overview
Register to unlock
Journal & Source
Register to unlock
Metadata & Integrity
Register to unlock